Edge dislocations are line defects in crystal lattices. Under applied shear stress, they glide along slip planes — the atomic mechanism of plastic deformation in metals.
Peierls-Nabarro model: dislocation moves when stress exceeds Peierls stress. Thermal activation enables glide below threshold (Arrhenius).